Molded body containing polycarbonate-polyorganosiloxane copolymer

ABSTRACT

Provided is a molded body including a polycarbonate-polyorganosiloxane copolymer which contains a polycarbonate block (A-1) formed of a repeating unit having a specific structure and a polyorganosiloxane block (A-2) containing a repeating unit having a specific structure, and in which the content of the polyorganosiloxane block (A-2) is from 20 mass % or more to 70 mass % or less, wherein the molded body has a durometer hardness of from 25 or more to 72 or less measured with a type D durometer in conformity with JIS K 6253-3:2012.

TECHNICAL FIELD

The present invention relates to a molded body that includes apolycarbonate-polyorganosiloxane copolymer, that has flexibility, andthat is excellent in transparency.

BACKGROUND ART

Resin molded articles having flexibility, which can be used by beingbonded to various shapes or by being deformed or processed in accordancewith various designs, have been required as a lighting cover or anoptical lens for a streetlight or the like. In such applications,transparency and mechanical characteristics are required in addition toflexibility.

Acrylic resin has been widely investigated as such resin because of itshigh transparency and optical characteristics (Patent Document 1).Although the acrylic resin is excellent in transparency and flexibility,the resin involves a drawback in that the resin is poor in mechanicalstrength, moldability, and handleability.

CITATION LIST Patent Document

Patent Document 1: JP 2003-277574 A

SUMMARY OF INVENTION Technical Problem

Polycarbonate-based resin is superior in mechanical strength andmoldability to the acrylic resin, but tends to be inferior inflexibility thereto.

An object of the present invention is to provide a molded body thatincludes a polycarbonate-polyorganosiloxane copolymer, and that has bothof excellent flexibility and transparency.

Solution to Problem

The inventors of the present invention have found that the incorporationof a polycarbonate-polyorganosiloxane copolymer (hereinafter sometimesabbreviated as “PC-POS copolymer”) having a specific structural unit andsatisfying a specific condition can provide a molded body havingflexibility and having excellent transparency.

That is, the present invention relates to the following items [1] to[10].

[1] A molded body, comprising a polycarbonate-polyorganosiloxanecopolymer (A) which contains a polycarbonate block (A-1) formed of arepeating unit represented by the following general formula (I) and apolyorganosiloxane block (A-2) containing a repeating unit representedby the following general formula (II), and in which a content of thepolyorganosiloxane block (A-2) is from 20 mass % or more to 70 mass % orless, wherein the molded body has a durometer hardness of from 25 ormore to 72 or less measured with a type D durometer in conformity withJIS K 6253-3:2012:

wherein R¹ and R² each independently represent a halogen atom, an alkylgroup having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6carbon atoms, X represents a single bond, an alkylene group having 1 to8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, acycloalkylene group having 5 to 15 carbon atoms, an arylene group having6 to 12 carbon atoms, a cycloalkylidene group having 5 to 15 carbonatoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbonatoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—,—SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogenatom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, analkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12carbon atoms, and “a” and “b” each independently represent an integer offrom 0 to 4.

[2] The molded body according to the above-mentioned item [1], wherein acontent of a unit represented by the following general formula (III) inthe polyorganosiloxane block (A-2) is 0.1 mol % or less:

wherein R³³ and R³⁴ each independently represent a hydrogen atom, ahalogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy grouphaving 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbonatoms, R³¹ represents an alkylene group having 1 to 8 carbon atoms, analkylidene group having 2 to 8 carbon atoms, a cycloalkylene grouphaving 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15carbon atoms, an arylene group having 6 to 12 carbon atoms, afluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms,or an arylalkylidene group having 7 to 15 carbon atoms, R³⁵ represents ahydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbonatoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl grouphaving 6 to 12 carbon atoms, and “t” represents an average chain lengthof a polyorganosiloxane.

[3] The molded body according to the above-mentioned item [1] or [2],wherein the polyorganosiloxane block (A-2) has a number of repetitionsof from 10 or more to less than 90.

[4] The molded body according to any one of the above-mentioned items[1] to [3], wherein the polyorganosiloxane block (A-2) contains a unitrepresented by at least one of the following general formula (II-I),(II-II), or (II-III):

wherein R³ to R⁶ each independently represent a hydrogen atom, a halogenatom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and aplurality of R³s, R⁴s, R⁵s, or R⁶s may be identical to or different fromeach other, Y represents —R⁷O—, —R⁷COO—, —R⁷NH—, —R⁷NR⁸—, —COO—, —S—,—R⁷COO—R⁹—O—, or —R⁷O—R¹⁰—O—, and a plurality of Ys may be identical toor different from each other, the R⁷ represents a single bond, a linear,branched, or cyclic alkylene group, an aryl-substituted alkylene group,a substituted or unsubstituted arylene group, or a diarylene group, R⁸represents an alkyl group, an alkenyl group, an aryl group, or anaralkyl group, R⁹ represents a diarylene group, R¹⁰ represents a linear,branched, or cyclic alkylene group, or a diarylene group, 8 represents adivalent group derived from a diisocyanate compound, or a divalent groupderived from a dicarboxylic acid or a halide of a dicarboxylic acid, “n”represents a chain length of a polyorganosiloxane, and n−1, and “p” and“q” each represent a number of repetitions of a polyorganosiloxane unitand each represent an integer of 1 or more, and a sum of “p” and “q” isn−2.

[5] The molded body according to any one of the above-mentioned items[1] to [4], wherein the polyorganosiloxane block (A-2) is represented bythe following general formula (V):

wherein R³ to R⁶ and n−1 are the same as those described in the generalformulae (II-I) to (II-III), and R¹⁵ represents a hydrogen atom, ahalogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy grouphaving 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbonatoms.

[6] The molded body according to any one of the above-mentioned items[1] to [5], wherein the polycarbonate-polyorganosiloxane copolymer (A)has a viscosity-average molecular weight of from 10,000 or more to23,000 or less.

[7] The molded body according to any one of the above-mentioned items[1] to [6], wherein the polycarbonate-polyorganosiloxane copolymer (A)has a molecular weight distribution of from 2.1 or more to 3.9 or less.

[8] The molded body according to any one of the above-mentioned items[1] to [7], wherein the molded body has a total light transmittance of75% or more measured in conformity with JIS K 7361-1:1997 when moldedinto a thickness of 2 mm.

[9] The molded body according to any one of the above-mentioned items[1] to [8], wherein the molded body is an optical member.

[10] The molded body according to any one of the above-mentioned items[1] to [8], wherein the molded body is at least one selected from aflexible display, a light guide plate, a housing, a water- oroil-repellent film, an optical adhesive, a switch cover, a heat sealingagent, a water stop material, a sealing agent, a connector, an adapter,a smartphone cover, a lens, a part for a pair of glasses or sunglasses,an optical fiber part, a cushion material for an on-vehicle battery, awiper blade, a traffic mirror, a side mirror, a rearview mirror, a lampcover, a bumper, a window, an exterior material, an interior material,an acoustic material, a steering wheel cover, a sensor cover, a watchpart, stationery, a cosmetic container, an aquarium for rearing anaquatic organism, a sole, a cup, a nail art material, a toy, a lure, asuction cup, cooking tools including a steamer, clothes, a siliconewiping sheet, a remote controller cover, an umbrella, a metal containerlining, a building material cover, a door, a window, a glass interlayer,a tent, a mirror, a shop window case, a plastic greenhouse, a medicalequipment housing, a transfusion bag, a transfusion tube, an injectionsyringe, a feeding bottle, a mask, a face belt, a filter part, a dampingpart, a robot housing, a drone housing, a shield, a bulletproof shield,a sport cushion, a window for an aircraft, a resin compatibilizer, alighting cover, a light guide, a light guide panel, a lighting unit, aprism panel, a flat lens, a Fresnel lens, a microlens array, and acollimator lens.

Advantageous Effects of Invention

According to the present invention, the molded body that includes apolycarbonate-polyorganosiloxane copolymer, and that has both ofexcellent flexibility and transparency can be obtained.

DESCRIPTION OF EMBODIMENTS

A molded body including a polycarbonate-polyorganosiloxane copolymer ofthe present invention is described in detail below. In this description,a specification considered to be preferred may be arbitrarily adopted,and it can be said that a combination of preferred specifications ismore preferred. The term “XX to YY” as used herein means “from XX ormore to YY or less.”

A molded body of the present invention is characterized by comprising apolycarbonate-polyorganosiloxane copolymer (A) which contains apolycarbonate block (A-1) formed of a repeating unit represented by thefollowing general formula (I) and a polyorganosiloxane block (A-2)containing a repeating unit represented by the following general formula(II), and in which a content of the polyorganosiloxane block (A-2) isfrom 20 mass % or more to 70 mass % or less, wherein the molded body hasa durometer hardness of from 25 or more to 72 or less measured with atype D durometer in conformity with JIS K 6253-3:2012:

wherein R¹ and R² each independently represent a halogen atom, an alkylgroup having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6carbon atoms, X represents a single bond, an alkylene group having 1 to8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, acycloalkylene group having 5 to 15 carbon atoms, an arylene group having6 to 12 carbon atoms, a cycloalkylidene group having 5 to 15 carbonatoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbonatoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—,—SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogenatom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, analkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12carbon atoms, and “a” and “b” each independently represent an integer offrom 0 to 4.

The polycarbonate-polyorganosiloxane copolymer (A) in the molded body ofthe present invention is described below. The polycarbonate block (A-1)represented by the general formula (I) is described in detail first. Inthe general formula (I), examples of the halogen atom that R¹ and R²each independently represent include a fluorine atom, a chlorine atom, abromine atom, and an iodine atom.

Examples of the alkyl group that R¹ and R² each independently representinclude a methyl group, an ethyl group, a n-propyl group, an isopropylgroup, various butyl groups (the term “various” means that a lineargroup and all kinds of branched groups are included, and the same holdstrue for the following), various pentyl groups, and various hexylgroups. Examples of the alkoxy group that R¹ and R² each independentlyrepresent include alkoxy groups having the above-mentioned alkyl groupsas alkyl group moieties.

Examples of the alkylene group represented by X include a methylenegroup, an ethylene group, a trimethylene group, a tetramethylene group,and a hexamethylene group. Among them, an alkylene group having 1 to 5carbon atoms is preferred. Examples of the alkylidene group representedby X include an ethylidene group and an isopropylidene group. Examplesof the cycloalkylene group represented by X include a cyclopentanediylgroup, a cyclohexanediyl group, and a cyclooctanediyl group. Among them,a cycloalkylene group having 5 to 10 carbon atoms is preferred. Examplesof the arylene group represented by X include a phenylene group, anaphthylene group, and a biphenylene group. Examples of thecycloalkylidene group represented by X include a cyclohexylidene group,a 3,5,5-trimethylcyclohexylidene group, and a 2-adamantylidene group.Among them, a cycloalkylidene group having 5 to 10 carbon atoms ispreferred, and a cycloalkylidene group having 5 to 8 carbon atoms ismore preferred. Examples of the aryl moiety of the arylalkylene grouprepresented by X include aryl groups each having 6 to 14 ring-formingcarbon atoms, such as a phenyl group, a naphthyl group, a biphenylgroup, and an anthryl group. Examples of the aryl moiety of thearylalkylidene group represented by X include aryl groups each having 6to 14 ring-forming carbon atoms, such as a phenyl group, a naphthylgroup, a biphenyl group, and an anthryl group.

“a” and “b” each independently represent an integer of from 0 to 4,preferably from 0 to 2, more preferably 0 or 1.

Among them, a block in which “a” and “b” each represent 0, and Xrepresents a single bond or an alkylene group having 1 to 8 carbonatoms, or a block in which “a” and “b” each represent 0, and Xrepresents an alkylidene group, in particular an isopropylidene group issuitable. The copolymer may contain a plurality of kinds ofpolycarbonate blocks as the polycarbonate blocks (A-1).

When the copolymer contains the plurality of kinds of polycarbonateblocks as the polycarbonate blocks (A-1), the content of a block inwhich “a” and “b” each represent 0, and X represents an isopropylidenegroup is preferably 90 mass % or more, more preferably 90.9 mass % ormore, still more preferably 93.3 mass % or more, particularly preferably95 mass % or more, most preferably 100 mass % from the viewpoint of thetransparency of the molded body.

Next, the polyorganosiloxane block (A-2) represented by the generalformula (II) is described in detail.

In the general formula (II), examples of the halogen atom that R³ and R⁴each independently represent include a fluorine atom, a chlorine atom, abromine atom, and an iodine atom. Examples of the alkyl group that R³and R⁴ each independently represent include a methyl group, an ethylgroup, a n-propyl group, an isopropyl group, various butyl groups,various pentyl groups, and various hexyl groups. Examples of the alkoxygroup that R³ and R⁴ each independently represent include alkoxy groupshaving the above-mentioned alkyl groups as alkyl group moieties.Examples of the aryl group that R³ and R⁴ each independently representinclude a phenyl group and a naphthyl group.

R³ and R⁴ each preferably represent a hydrogen atom, an alkyl grouphaving 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms,or an aryl group having 6 to 12 carbon atoms, and each more preferablyrepresent a methyl group.

The polyorganosiloxane block containing the repeating unit representedby the general formula (II) preferably has a unit represented by any oneof the following general formulae (II-I), (II-II) or (II-III):

wherein R³ to R⁶ each independently represent a hydrogen atom, a halogenatom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and aplurality of R³s, R⁴s, R⁵s, or R⁶s may be identical to or different fromeach other, Y represents —R⁷O—, —R⁷COO—, —R⁷NH—, —R⁷NR⁸—, —COO—, —S—,—R⁷COO—R⁹—O—, or —R⁷O—R¹⁰—O—, and a plurality of Ys may be identical toor different from each other, the R⁷ represents a single bond, a linear,branched, or cyclic alkylene group, an aryl-substituted alkylene group,a substituted or unsubstituted arylene group, or a diarylene group, R⁸represents an alkyl group, an alkenyl group, an aryl group, or anaralkyl group, R⁹ represents a diarylene group, R¹⁰ represents a linear,branched, or cyclic alkylene group, or a diarylene group, 8 represents adivalent group derived from a diisocyanate compound, or a divalent groupderived from a dicarboxylic acid or a halide of a dicarboxylic acid, “n”represents the average chain length of a polyorganosiloxane, and n−1,and “p” and “q” each represent the number of repetitions of apolyorganosiloxane unit and each represent an integer of 1 or more, andthe sum of “p” and “q” is n−2.

Examples of the halogen atom that R³ to R⁶ each independently representinclude a fluorine atom, a chlorine atom, a bromine atom, and an iodineatom. Examples of the alkyl group that R³ to R⁶ each independentlyrepresent include a methyl group, an ethyl group, a n-propyl group, anisopropyl group, various butyl groups, various pentyl groups, andvarious hexyl groups. Examples of the alkoxy group that R³ to R⁶ eachindependently represent include alkoxy groups having the above-mentionedalkyl groups as alkyl group moieties. Examples of the aryl group that R³to R⁶ each independently represent include a phenyl group and a naphthylgroup.

R³ to R⁶ each preferably represent a hydrogen atom, an alkyl grouphaving 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms,or an aryl group having 6 to 12 carbon atoms.

R³ to R⁶ in the general formula (II-I), the general formula (II-II),and/or the general formula (II-III) each preferably represent a methylgroup.

The linear or branched alkylene group represented by R⁷ in —R⁷O—,—R⁷COO—, —R⁷NH—, —R⁷NR⁸—, —R⁷COO—R⁹—O—, or —R⁷O—R¹⁰—O— represented by Yis, for example, an alkylene group having 1 to 8 carbon atoms,preferably 1 to 5 carbon atoms, and the cyclic alkylene grouprepresented by R⁷ is, for example, a cycloalkylene group having 5 to 15carbon atoms, preferably 5 to 10 carbon atoms.

The aryl-substituted alkylene group represented by R⁷ may have asubstituent, such as an alkoxy group or an alkyl group, on its aromaticring, and a specific structure thereof may be, for example, a structurerepresented by the following general formula (i) or (ii). When the blockhas the aryl-substituted alkylene group, the alkylene group is bonded toSi.

wherein “c” represents a positive integer and typically represents aninteger of from 1 to 6.

The diarylene group represented by any one of R⁷, R⁹, and R¹⁰ refers toa group in which two arylene groups are linked to each other directly orthrough a divalent organic group, and is specifically a group having astructure represented by —Ar¹—W—Ar²—. Ar¹ and Ar² each represent anarylene group, and W represents a single bond or a divalent organicgroup. Examples of the divalent organic group represented by W includean isopropylidene group, a methylene group, a dimethylene group, and atrimethylene group.

Examples of the arylene group represented by any one of R⁷, Ar¹, and Ar²include arylene groups each having 6 to 14 ring-forming carbon atoms,such as a phenylene group, a naphthylene group, a biphenylene group, andan anthrylene group. Those arylene groups may each have an arbitrarysubstituent, such as an alkoxy group or an alkyl group.

The alkyl group represented by R⁸ is a linear or branched group having 1to 8, preferably 1 to 5 carbon atoms. The alkenyl group represented byR⁸ is, for example, a linear or branched group having 2 to 8, preferably2 to 5 carbon atoms. The aryl group represented by R⁸ is, for example, aphenyl group or a naphthyl group. The aralkyl group represented by R⁸is, for example, a phenylmethyl group or a phenylethyl group.

The linear, branched, or cyclic alkylene group represented by R¹⁰ is thesame as that represented by R⁷.

Y preferably represents —R⁷O—. R⁷ preferably represents anaryl-substituted alkylene group, in particular, a residue of aphenol-based compound having an alkyl group, and more preferablyrepresents an organic residue derived from allylphenol or an organicresidue derived from eugenol.

With regard to “p” and “q” in the formula (II-II), it is preferred thatp=q.

β represents a divalent group derived from a diisocyanate compound, or adivalent group derived from a dicarboxylic acid or a halide of adicarboxylic acid, and examples thereof include divalent groupsrepresented by the following general formulae (iii) to (vii).

It is more preferred that the PC-POS copolymer (A) in the molded body ofthe present invention contain the polyorganosiloxane block (A-2)represented by the following structural formula:

wherein R³ to R⁶ and “n” are the same as those described in the generalformulae (II-I) to (II-III), and R¹⁵ represents a hydrogen atom, ahalogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy grouphaving 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbonatoms.

The number of repetitions of the polyorganosiloxane block (A-2) in thePC-POS copolymer is preferably from 10 or more to less than 90. Morespecifically, the number of repetitions is preferably 10 or more, morepreferably 15 or more, particularly preferably 20 or more, and ispreferably less than 90, more preferably 80 or less, still morepreferably 60 or less, still further more preferably 45 or less, stillfurther more preferably 40 or less, particularly preferably less than40. The number of repetitions is calculated by nuclear magneticresonance (NMR) measurement. When the number of repetitions of thepolyorganosiloxane block (A-2) is set within the range, both ofexcellent transparency and flexibility can be achieved, and peelingafter the production of the molded body can be suppressed.

The content of the polyorganosiloxane block (A-2) in the PC-POScopolymer (A) in the molded body of the present invention needs to befrom 20 mass % or more to 70 mass % or less. When the content of thepolyorganosiloxane block (A-2) in the PC-POS copolymer is 20 mass % ormore, a copolymer excellent in flexibility can be obtained. When thecontent of the polyorganosiloxane block (A-2) is 70 mass % or less, acopolymer that is free of any remarkable tackiness, and that canmaintain a shape as a flexible molded body is obtained.

The content of the polyorganosiloxane block (A-2) in the PC-POScopolymer (A) in the molded body of the present invention is preferably30 mass % or more, more preferably 40 mass % or more, still morepreferably 45 mass % or more, and is preferably 65 mass % or less, morepreferably 60 mass % or less, still more preferably 55 mass % or less.

The viscosity-average molecular weight of the PC-POS copolymer in themolded body of the present invention is preferably from 10,000 or moreto 23,000 or less. The viscosity-average molecular weight (Mv) may beadjusted by using a molecular weight modifier (terminal stopper) or thelike, or by a reaction condition. The viscosity-average molecular weightis preferably set within the range because a copolymer excellent inmoldability is obtained, and hence the melt fracture of the molded bodycan be further suppressed.

The viscosity-average molecular weight (Mv) is more preferably 12,000 ormore, still more preferably 14,000 or more, still further morepreferably 16,000 or more, and is more preferably 21,500 or less, stillmore preferably 20,500 or less, still further more preferably 19,500 orless, still further more preferably 18,500 or less, particularlypreferably 18,000 or less. When the viscosity-average molecular weightis 10,000 or more, a sufficient molded article strength can be obtained.

The viscosity-average molecular weight (Mv) is a value calculated fromthe following Schnell's equation by measuring the limiting viscosity [₄]of a methylene chloride solution at 20° C.

[η]=1.23×10⁻⁵ ×mv ^(0.83)

The weight-average molecular weight (Mw) of the PC-POS copolymer of thepresent invention is preferably 40,000 or less. When the weight-averagemolecular weight (Mw) falls within the range, a PC-POS copolymerexcellent in flexibility can be obtained. The weight-average molecularweight (Mw) of the PC-POS copolymer is more preferably 37,000 or less,still more preferably 35,000 or less, still further more preferably30,000 or less. In addition, the weight-average molecular weight (Mw) ispreferably 20,000 or more, more preferably 23,000 or more.

Further, the molecular weight distribution (Mw/Mn) of the PC-POScopolymer (A) in the molded body of the present invention is preferablyfrom 2.1 or more to 3.9 or less. The molecular weight distribution Mw/Mnof the PC-POS copolymer preferably falls within the range becausenonuniformity due to an irregular flow or a phase separation issuppressed at the time of the molding of the copolymer, and hence amolded body that has high transparency, and that is easily controlled inflexibility is obtained.

The molecular weight distribution Mw/Mn of the PC-POS copolymer (A) ismore preferably 2.3 or more, still more preferably 2.4 or more, stillfurther more preferably 2.5 or more, still further more preferably 2.7or more, particularly preferably 2.8 or more, and is more preferably 3.5or less, still more preferably 3.0 or less, particularly preferably 2.9or less.

The PC-POS copolymer (A) may be produced by a known production method,such as an interfacial polymerization method (phosgene method), apyridine method, or an ester exchange method. In particular, theinterfacial polymerization method including adding a polyorganosiloxaneto a reaction system in which a dihydric phenol and a carbonateprecursor are polymerized to copolymerize the materials is preferablyadopted because of the following reason: a step of separating an organicphase containing the PC-POS copolymer and an aqueous phase containing anunreacted product, a catalyst residue, or the like becomes easier, andhence the separation of the organic phase containing the PC-POScopolymer and the aqueous phase in each washing step based on alkaliwashing, acid washing, or pure water (ion-exchanged water) washingbecomes easier, thereby efficiently providing the PC-POS copolymer. Withregard to a method of producing the PC-POS copolymer, reference may bemade to, for example, a method described in JP 2014-80462 A.

Specifically, the PC-POS copolymer may be produced by: dissolving apolycarbonate oligomer produced in advance to be described later and apolyorganosiloxane in a water-insoluble organic solvent (e.g., methylenechloride); adding a solution of a dihydric phenol-based compound (e.g.,bisphenol A) in an aqueous alkali compound (e.g., aqueous sodiumhydroxide) to the solution; and subjecting the mixture to an interfacialpolycondensation reaction through the use of a tertiary amine (e.g.,triethylamine) or a quaternary ammonium salt (e.g.,trimethylbenzylammonium chloride) as a polymerization catalyst in thepresence of a terminal stopper (a monohydric phenol, such asp-tert-butylphenol). In addition, the PC-POS copolymer may also beproduced by copolymerizing the polyorganosiloxane and a dihydric phenol,and phosgene, a carbonate ester, or a chloroformate.

When the PC-POS copolymer (A) in the molded body of the presentinvention is produced by, for example, causing a polycarbonate oligomerand a polyorganosiloxane raw material to react with each other in anorganic solvent, and then causing the resultant to react with a dihydricphenol, the solid content weight (g/L) of the polycarbonate oligomer in1 L of a mixed solution of the organic solvent and the polycarbonateoligomer preferably falls within the range of 200 g/L or less from theviewpoint of the transparency of the PC-POS copolymer to be obtained.The solid content weight is more preferably 180 g/L or less, still morepreferably 170 g/L or less.

The transparency of the copolymer to be obtained becomes moresatisfactory as the solid content weight (g/L) of the polycarbonateoligomer in 1 L of the mixed solution of the organic solvent and thepolycarbonate oligomer reduces. Accordingly, the lower limit of thesolid content weight is not particularly limited. However, from theviewpoint of efficiently producing the PC-POS copolymer, the solidcontent weight is preferably 20 g/L or more, more preferably 30 g/L ormore, still more preferably 40 g/L or more.

A polyorganosiloxane represented by the following general formula (1),general formula (2), and/or general formula (3) may be used as thepolyorganosiloxane serving as a raw material:

wherein

R³ to R⁶, Y, β, n−1, “p”, and “q” are as described above, and specificexamples and preferred examples thereof are also the same as thosedescribed above, and

Z represents a hydrogen atom or a halogen atom, and a plurality of Zsmay be identical to or different from each other.

Examples of the polyorganosiloxane represented by the general formula(1) include compounds each represented by any one of the followinggeneral formulae (1-1) to (1-11):

wherein in the general formulae (1-1) to (1-11), R³ to R⁶, “n”, and R⁸are as defined above, and preferred examples thereof are also the sameas those described above, and “c” represents a positive integer andtypically represents an integer of from 1 to 6.

Among them, a phenol-modified polyorganosiloxane represented by thegeneral formula (1-1) is preferred from the viewpoint of its ease ofpolymerization. Anα,ω-bis[3-(o-hydroxyphenyl)propyl]polydimethylsiloxane, which is onecompound represented by the general formula (1-2), or anα,ω-bis[3-(4-hydroxy-3-methoxyphenyl)propyl]polydimethylsiloxane, whichis one compound represented by the general formula (1-3), is preferredfrom the viewpoint of its ease of availability.

In addition to the foregoing, a compound having a structure representedby the following general formula (4) may be used as a polyorganosiloxaneraw material:

wherein R³ and R⁴ are identical to those described above. The averagechain length of the polyorganosiloxane block represented by the generalformula (4) is (r×m), and the range of the (r×m) is the same as that ofthe “n”.

When the compound represented by the general formula (4) is used as apolyorganosiloxane raw material, the polyorganosiloxane block (A-2)preferably has a unit represented by the following general formula(II-IV):

wherein R³, R⁴, “r”, and “m” are as described above.

The copolymer may include a structure represented by the followinggeneral formula (II-V) as the polyorganosiloxane block (A-2):

wherein R¹⁸ to R²¹ each independently represent a hydrogen atom or analkyl group having 1 to 13 carbon atoms, R²² represents an alkyl grouphaving 1 to 6 carbon atoms, a hydrogen atom, a halogen atom, a hydroxygroup, an alkoxy group having 1 to 6 carbon atoms, or an aryl grouphaving 6 to 14 carbon atoms, Q² represents a divalent aliphatic grouphaving 1 to 10 carbon atoms, and n−1 represents the number ofrepetitions of the polyorganosiloxane block, and its range is asdescribed above.

In the general formula (II-V), examples of the alkyl group having 1 to13 carbon atoms that R¹⁸ to R²¹ each independently represent include amethyl group, an ethyl group, a n-propyl group, an isopropyl group,various butyl groups, various pentyl groups, various hexyl groups,various heptyl groups, various octyl groups, a 2-ethylhexyl group,various nonyl groups, various decyl groups, various undecyl groups,various dodecyl groups, and various tridecyl groups. Among them, R¹⁸ toR²¹ each preferably represent a hydrogen atom or an alkyl group having 1to 6 carbon atoms, and it is more preferred that all of R¹⁸ to R²¹ eachrepresent a methyl group.

Examples of the alkyl group having 1 to 6 carbon atoms represented byR²² include a methyl group, an ethyl group, a n-propyl group, anisopropyl group, various butyl groups, various pentyl groups, andvarious hexyl groups. Examples of the halogen atom represented by R²²include a fluorine atom, a chlorine atom, a bromine atom, and an iodineatom. An example of the alkoxy group having 1 to 6 carbon atomsrepresented by R²² is an alkoxy group whose alkyl group moiety is thealkyl group described above. Examples of the aryl group having 6 to 14carbon atoms represented by R²² include a phenyl group, a toluyl group,a dimethylphenyl group, and a naphthyl group.

Among them, R²² preferably represents a hydrogen atom or an alkoxy grouphaving 1 to 6 carbon atoms, more preferably represents a hydrogen atomor an alkoxy group having 1 to 3 carbon atoms, and still more preferablyrepresents a hydrogen atom.

The divalent aliphatic group having 1 to 10 carbon atoms represented byQ² is preferably a linear or branched divalent saturated aliphatic grouphaving 1 to 10 carbon atoms. The number of carbon atoms of the saturatedaliphatic group is preferably from 1 to 8, more preferably from 2 to 6,still more preferably from 3 to 6, still further more preferably from 4to 6. The number of repetitions n−1 is as described above.

A preferred mode of the constituent unit (II-V) may be, for example, astructure represented by the following general formula (II-VI):

wherein n−1 is identical to that described above.

The polyorganosiloxane block (A-2) represented by the general formula(II-V) or (II-VI) may be obtained by using a polyorganosiloxane rawmaterial represented by the following general formula (5) or (6):

wherein R¹⁸ to R²², Q², and n−1 are as described above;

wherein n−1 is as described above.

A method of producing the polyorganosiloxane is not particularlylimited. According to, for example, a method described in JP 11-217390A, a crude polyorganosiloxane may be obtained by: causingcyclotrisiloxane and disiloxane to react with each other in the presenceof an acid catalyst to synthesize α,ω-dihydrogen organopentasiloxane;and then subjecting the α,ω-dihydrogen organopentasiloxane to anaddition reaction with, for example, a phenolic compound (e.g.,2-allylphenol, 4-allylphenol, eugenol, or 2-propenylphenol) in thepresence of a catalyst for a hydrosilylation reaction. According to amethod described in JP 2662310 B2, the crude polyorganosiloxane may beobtained by: causing octamethylcyclotetrasiloxane andtetramethyldisiloxane to react with each other in the presence ofsulfuric acid (acid catalyst); and subjecting the resultantα,ω-dihydrogen organopolysiloxane to an addition reaction with thephenolic compound or the like in the presence of the catalyst for ahydrosilylation reaction in the same manner as that described above. Theα,ω-dihydrogen organopolysiloxane may be used after its chain length “n”has been appropriately adjusted in accordance with its polymerizationconditions, or a commercial α,ω-dihydrogen organopolysiloxane may beused. A catalyst described in JP 2016-098292 A may be specifically usedas the hydrosilylation catalyst.

The polycarbonate oligomer may be produced by a reaction between adihydric phenol and a carbonate precursor, such as phosgene ortriphosgene, in an organic solvent, such as methylene chloride,chlorobenzene, or chloroform. When the polycarbonate oligomer isproduced by using an ester exchange method, the oligomer may be producedby a reaction between the dihydric phenol and a carbonate precursor,such as diphenyl carbonate.

A dihydric phenol represented by the following general formula (viii) ispreferably used as the dihydric phenol:

wherein R¹, R², “a”, “b”, and X are as described above.

Examples of the dihydric phenol represented by the general formula(viii) include: bis(hydroxyphenyl)alkane-based dihydric phenols, such as2,2-bis(4-hydroxyphenyl)propane [bisphenol A],bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, and2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane; 4,4′-dihydroxydiphenyl;bis(4-hydroxyphenyl)cycloalkanes; bis(4-hydroxyphenyl) oxide;bis(4-hydroxyphenyl) sulfide; bis(4-hydroxyphenyl) sulfone;bis(4-hydroxyphenyl) sulfoxide; and bis(4-hydroxyphenyl) ketone. Thosedihydric phenols may be used alone or as a mixture thereof.

Among them, bis(hydroxyphenyl)alkane-based dihydric phenols arepreferred, and bisphenol A is more preferred. When bisphenol A is usedas the dihydric phenol, the PC-POS copolymer is such that in the generalformula (i), X represents an isopropylidene group and a=b=0.

Examples of the dihydric phenol except bisphenol A includebis(hydroxyaryl)alkanes, bis(hydroxyaryl)cycloalkanes, dihydroxyarylethers, dihydroxydiaryl sulfides, dihydroxydiaryl sulfoxides,dihydroxydiaryl sulfones, dihydroxydiphenyls, dihydroxydiaryl fluorenes,and dihydroxydiaryl adamantanes. Those dihydric phenols may be usedalone or as a mixture thereof.

Examples of the bis(hydroxyaryl)alkanes includebis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane,2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)octane,bis(4-hydroxyphenyl)phenylmethane, bis(4-hydroxyphenyl)diphenylmethane,2,2-bis(4-hydroxy-3-methylphenyl)propane,bis(4-hydroxyphenyl)naphthylmethane,1,1-bis(4-hydroxy-3-tert-butylphenyl)propane,2,2-bis(4-hydroxy-3-bromophenyl)propane,2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane,2,2-bis(4-hydroxy-3-chlorophenyl)propane,2,2-bis(4-hydroxy-3,5-dichlorophenyl)propane, and2,2-bis(4-hydroxy-3,5-dibromophenyl)propane.

Examples of the bis(hydroxyaryl)cycloalkanes include1,1-bis(4-hydroxyphenyl)cyclopentane,1,1-bis(4-hydroxyphenyl)cyclohexane,1,1-bis(4-hydroxyphenyl)-3,5,5-trimethylcyclohexane,2,2-bis(4-hydroxyphenyl)norbornane, and1,1-bis(4-hydroxyphenyl)cyclododecane. Examples of the dihydroxyarylethers include 4,4′-dihydroxydiphenyl ether and4,4′-dihydroxy-3,3′-dimethylphenyl ether.

Examples of the dihydroxydiaryl sulfides include 4,4′-dihydroxydiphenylsulfide and 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfide. Examples ofthe dihydroxydiaryl sulfoxides include 4,4′-dihydroxydiphenyl sulfoxideand 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfoxide. Examples of thedihydroxydiaryl sulfones include 4,4′-dihydroxydiphenyl sulfone and4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfone.

An example of the dihydroxydiphenyls is 4,4′-dihydroxydiphenyl. Examplesof the dihydroxydiarylfluorenes include 9,9-bis(4-hydroxyphenyl)fluoreneand 9,9-bis(4-hydroxy-3-methylphenyl)fluorene. Examples of thedihydroxydiaryladamantanes include 1,3-bis(4-hydroxyphenyl)adamantane,2,2-bis(4-hydroxyphenyl)adamantane, and1,3-bis(4-hydroxyphenyl)-5,7-dimethyladamantane.

Examples of dihydric phenols except those described above include4,4′-[1,3-phenylenebis(1-methylethylidene)]bisphenol,10,10-bis(4-hydroxyphenyl)-9-anthrone, and1,5-bis(4-hydroxyphenylthio)-2,3-dioxapentane.

In order to adjust the molecular weight of the PC-POS copolymer to beobtained, a terminal stopper (molecular weight modifier) may be used.Examples of the terminal stopper may include monohydric phenols, such asphenol, p-cresol, p-tert-butylphenol, p-tert-octylphenol, p-cumylphenol,p-nonylphenol, m-pentadecylphenol, and p-tert-amylphenol. Thosemonohydric phenols may be used alone or in combination thereof.

After the interfacial polycondensation reaction, the PC-POS copolymer(A) in the molded body of the present invention may be obtained byappropriately leaving the resultant at rest to separate the resultantinto an aqueous phase and an organic solvent phase [separating step],washing the organic solvent phase (preferably washing the phase with abasic aqueous solution, an acidic aqueous solution, and water in thestated order) [washing step], concentrating the resultant organic phase[concentrating step], and drying the concentrated phase [drying step].

In the PC-POS copolymer (A) in the molded body of the present invention,the content of a unit represented by the following general formula (III)in the polyorganosiloxane block (A-2) is preferably 0.1 mol % or less:

wherein R³³ and R³⁴ each independently represent a hydrogen atom, ahalogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy grouphaving 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbonatoms, R³¹ represents an alkylene group having 1 to 8 carbon atoms, analkylidene group having 2 to 8 carbon atoms, a cycloalkylene grouphaving 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15carbon atoms, an arylene group having 6 to 12 carbon atoms, afluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms,or an arylalkylidene group having 7 to 15 carbon atoms, R³⁵ represents ahydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbonatoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl grouphaving 6 to 12 carbon atoms, and “t” represents the average chain lengthof a polyorganosiloxane.

When the content of the block represented by the general formula (III)is 0.1 mol % or less, precise control between the raw materialpolyorganosiloxane to be used at the time of the production of thePC-POS copolymer and the chain length of the copolymer can be performed,and hence a target molded body having both of high flexibility andtransparency can be obtained.

Specifically, the PC-POS copolymer in which the content of the blockrepresented by the general formula (III) is 0.1 mol % or less can beobtained by adopting the above-mentioned interfacial polymerizationmethod. The block represented by the general formula (III) may not betheoretically incorporated into the PC-POS copolymer (A) in the moldedbody of the present invention in terms of synthesis procedure, and henceits content is substantially 0.0 mol %.

A method of quantifying the content is described in detail. The contentof the block represented by the general formula (III) in the PC-POScopolymer (A) is quantified by a peak in ¹³C-NMR. A specificquantification method is described in Examples. The quantification lowerlimit of the quantification method is calculated to be less than 0.1 mol% by the baseline SN ratio of a ¹³C-NMR chart. The semi-quantificationof a region below 0.1 mol % is possible, though the quantificationthereof is impossible. At the time of the semi-quantification, relativecomparison between the heights of peaks corresponding to the generalformula (III) is performed. When the relative comparison between thepeak heights is difficult, the lower limit that can be semi-quantifiedcan be further lowered by further increasing the number of scans toincrease the SN ratio.

The content of the block represented by the general formula (III) in thePC-POS copolymer (A) in the molded body of the present invention, thecontent being specified by the quantification method or thesemi-quantification method described in the foregoing, is morepreferably 0.08 mol % or less, still more preferably 0.05 mol % or less,particularly preferably substantially 0.0 mol %.

In a conventionally known synthesis method, a polymerization-activephosgene gas is caused to react with a mixture of a bisphenol monomerand a polyorganosiloxane monomer, or with a polyorganosiloxane.Accordingly, even when the amount of the block represented by thegeneral formula (III) is reduced by improving a method of adding thephosgene gas and the time period of contact between the gas and themixture or the polyorganosiloxane, contact between a plurality ofpolyorganosiloxane monomer molecules and the polymerization-activephosgene gas is inevitable, and hence it is impossible to set the amountof the block represented by the general formula (III) to substantially0.0 mol %.

Meanwhile, in the method of synthesizing the PC-POS copolymer in themolded body of the present invention, a bisphenol monomer and a phosgenegas are caused to react with each other in advance to synthesize abisphenol monomer or a bisphenol polycarbonate oligomer both terminalsof which are chloroformate structures, and a polymerization-inactivepolyorganosiloxane monomer is, or the polymerization-inactivepolyorganosiloxane monomer and a polymerization-inactive bisphenolmonomer are, caused to react with the bisphenol monomer havingpolymerization-active chloroformate groups at both of its terminals orthe bisphenol polycarbonate oligomer having polymerization-activechloroformate groups at both of its terminals. Accordingly, the blockrepresented by the general formula (III) may be substantially free frombeing produced.

A raw material pellet may be obtained by melt-kneading the PC-POScopolymer to be obtained. At that time, any other additive may be addedat the time of the preparation of the raw material pellet to the extentthat the effects of the present invention are not impaired. Examples ofthe other additive may include an antioxidant, a UV absorber, a releaseagent, a reinforcing material, a filler, an elastomer for an impactresistance improvement, a dye, a pigment, an antistatic agent, and otherresins except the polycarbonate, and the addition amount may also beappropriately selected at an appropriate ratio.

The melt-kneading may be performed by a method involving premixing witha typically used apparatus, such as a ribbon blender or a drum tumbler,and using, for example, a Henschel mixer, a Banbury mixer, asingle-screw extruder, a twin-screw extruder, a multi-screw extruder, ora Ko-kneader. In normal cases, a heating temperature at the time of thekneading is appropriately selected from the range of from 240° C. ormore to 320° C. or less. An extruder, in particular, a vented extruderis preferably used in the melt-kneading.

<Molded Body>

The molded body of the present invention may be produced by any one of,for example, an injection molding method, an injection compressionmolding method, an extrusion molding method, a blow molding method, apress molding method, a vacuum molding method, and an expansion moldingmethod through the use of the melt-kneadedpolycarbonate-polyorganosiloxane copolymer or the resultant pelletdescribed above as a raw material. In particular, the molded body of thepresent invention is preferably a molded body obtained by using thepellet of the PC-POS copolymer (A) obtained through the melt-kneading.

The molded body of the present invention is characterized by having bothof excellent flexibility and transparency. The respective properties aredescribed in detail.

The flexibility is described in detail. The durometer hardness of themolded body of the present invention measured with a type D durometer inconformity with JIS K 6253-3:2012 by a method described in Examplesneeds to be from 25 or more to 72 or less.

The durometer hardness is an indicator representing an indentationhardness. To obtain a molded body having high flexibility whilemaintaining some degree of mechanical strength, the type D durometerhardness needs to fall within the above-mentioned range. The molded bodyof the present invention including the specific PC-POS copolymer (A) isexcellent in flexibility, and hence can, for example, be used as alighting cover without through any packing member and correspond to alight guide having a complicated shape. Accordingly, ease ofconstruction can be drastically improved. Further, even in the case ofan optical member having a void structure having an undercut draft angletherein, the molded body and the optical member can be integrally moldedwithout the performance of any internal cutting step, and hence themolded body can be suitably used in a collimator lens. The molded bodyis excellent in transparency and flexibility, and hence may be suitablyused in, for example, the following materials: household electricappliance-related materials, such as a substrate, a light guide plate,or a housing for a flexible display, a water- or oil-repellent film, anoptical adhesive, a switch cover, a heat sealing agent, a water stopmaterial, a sealing agent, a connector, an adapter, and a smartphonecover; materials for optical applications, such as a lens, a part for apair of glasses or sunglasses, and an optical fiber part;automobile-related materials, such as a cushion material for anon-vehicle battery, a wiper blade, a traffic mirror, a side mirror, arearview mirror, a lamp cover, a bumper, a window, a glass interlayer,an exterior material, an interior material, an acoustic material, asteering wheel cover, and a sensor cover; commodities, such as a watchpart, stationery, a cosmetic container, an aquarium for rearing anaquatic organism, a sole, a cup, a nail art material, a toy, a lure, asuction cup, cooking tools including a steamer, clothes, a siliconewiping sheet, a remote controller cover, an umbrella, and a metalcontainer lining; building-related materials, such as a buildingmaterial cover, a door, a window, a glass interlayer, a tent, a mirror,a shop window case, and a plastic greenhouse; medical materials, such asa medical equipment housing, a transfusion bag, a transfusion tube, aninjection syringe, a feeding bottle, a mask, a face belt, and a filterpart; and other materials, such as a damping part, a robot housing, adrone housing, a shield, a bulletproof shield, a sport cushion, a windowfor an aircraft, and a resin compatibilizer.

The durometer hardness of the molded body of the present inventionmeasured with a type D durometer is more preferably 30 or more, stillmore preferably 40 or more, and is more preferably 70 or less, stillmore preferably 68 or less.

The preferred range of the durometer hardness may vary depending on anapplication where the molded body of the present application is used.For example, when the molded body is used in an application whereemphasis is placed on flexibility, the hardness is more preferably 28 ormore, and is more preferably 33 or less. When the molded body is used inan application where emphasis is placed on a mechanical strength, thehardness is more preferably 60 or more, and is more preferably 65 orless. In addition to the foregoing, when the molded body is used in anapplication where emphasis is placed on both of the flexibility and themechanical strength, the hardness is more preferably 45 or more, and ismore preferably 50 or less.

The durometer hardness of the molded body cannot be measured in somecases depending on the shape thereof. In any such case, however, thedurometer hardness can be measured by: melting the molded body once; andmolding the molten product into a shape whose durometer hardness can bemeasured again. Molding conditions in the case are the same as those ofa molding method described in Examples.

A product obtained by, for example, cutting, decomposing, or breakingany one of such molded body and a member including the molded body maybe used as a raw material for obtaining the molded body.

The transparency is described in detail. It is preferred that the moldedbody of the present invention have a total light transmittance of 75% ormore measured in conformity with JIS K 7361-1:1997 when molded into athickness of 2 mm. When the total light transmittance under thecondition is 75% or more, the molded body is excellent in transparency,and hence can be suitably used as the above-mentioned opticaltransparent member.

The total light transmittance of the molded body of the presentinvention when molded into a thickness of 2 mm is more preferably 85% ormore, still more preferably 89% or more, still further more preferably90% or more, still further more preferably 91% or more, particularlypreferably 92% or more.

The molded body of the present invention may be used as an opticalmember or a transparent member. Specifically, the molded body may besuitably used in at least one selected from, for example, a flexibledisplay, a light guide plate, a housing, a water- or oil-repellent film,an optical adhesive, a switch cover, a heat sealing agent, a water stopmaterial, a sealing agent, a connector, an adapter, a smartphone cover,a lens, a part for a pair of glasses or sunglasses, an optical fiberpart, a cushion material for an on-vehicle battery, a wiper blade, atraffic mirror, a side mirror, a rearview mirror, a lamp cover, abumper, a window, an exterior material, an interior material, anacoustic material, a steering wheel cover, a sensor cover, a watch part,stationery, a cosmetic container, an aquarium for rearing an aquaticorganism, a sole, a cup, a nail art material, a toy, a lure, a suctioncup, cooking tools including a steamer, clothes, a silicone wipingsheet, a remote controller cover, an umbrella, a metal container lining,a building material cover, a door, a window, a glass interlayer, a tent,a mirror, a shop window case, a plastic greenhouse, a medical equipmenthousing, a transfusion bag, a transfusion tube, an injection syringe, afeeding bottle, a mask, a face belt, a filter part, a damping part, arobot housing, a drone housing, a shield, a bulletproof shield, a sportcushion, a window for an aircraft, a resin compatibilizer, a lightingcover, a light guide, a light guide panel, a lighting unit, a prismpanel, a flat lens, a Fresnel lens, a microlens array, and a collimatorlens.

EXAMPLES

The present invention is more specifically described by way of Examples.However, the present invention is by no means limited by these Examples.In each of Examples, characteristic values and evaluation results weredetermined in the following manner.

(1) Chain Length and Content of Polydimethylsiloxane

The chain length and content of a polydimethylsiloxane were calculatedby NMR measurement from the integrated value ratio of a methyl group ofthe polydimethylsiloxane. In this description, the polydimethylsiloxaneis sometimes abbreviated as PDMS.

<Quantification Method for Chain Length of Polydimethylsiloxane> ¹H-NMRMeasurement Conditions

NMR apparatus: ECA500 manufactured by JEOL Resonance Co., Ltd.

Probe: 50TH5AT/FG2

Observed range: −5 ppm to 15 ppmObservation center: 5 ppmPulse repetition time: 9 secPulse width: 45°NMR sample tube: 5 φSample amount: 30 mg to 40 mgSolvent: deuterochloroformMeasurement temperature: room temperatureNumber of scans: 256 times

Allylphenol-terminated Polydimethylsiloxane

A: an integrated value of a methyl group in a dimethylsiloxane moietyobserved around δ −0.02 to δ 0.5B: an integrated value of a methylene group in allylphenol observedaround δ 2.50 to δ 2.75

Chain length of polydimethylsiloxane=(A/6)/(B/4)

Eugenol-terminated Polydimethylsiloxane

A: an integrated value of a methyl group in a dimethylsiloxane moietyobserved around δ −0.02 to δ 0.5B: an integrated value of a methylene group in eugenol observed around δ2.40 to δ 2.70

Chain length of polydimethylsiloxane=(A/6)/(B/4)

<Quantification Method for Content of Polydimethylsiloxane>

Quantification method for the copolymerization amount of apolydimethylsiloxane in a PTBP-terminated polycarbonate obtained bycopolymerizing an allylphenol-terminated polydimethylsiloxane

NMR apparatus: ECA500 manufactured by JEOL Resonance Co., Ltd.

Probe: 50TH5AT/FG2

Observed range: −5 ppm to 15 ppmObservation center: 5 ppmPulse repetition time: 9 secPulse width: 45°Number of scans: 256 timesNMR sample tube: 5 φSample amount: 30 mg to 40 mgSolvent: deuterochloroformMeasurement temperature: room temperatureA: an integrated value of a methyl group in a BPA moiety observed aroundδ 1.5 to δ 1.9B: an integrated value of a methyl group in a dimethylsiloxane moietyobserved around δ −0.02 to δ 0.3C: an integrated value of a butyl group in a p-tert-butylphenyl moietyobserved around δ 1.2 to δ 1.4

a=A/6

b=B/6

c=C/9

T=a+b+c

f=a/T×100

g=b/T×100

h=c/T×100

TW=f×254+g×74.1+h×149

PDMS (wt %)=g×74.1/TW×100

<Quantification Method for Amount of Block Represented by Formula (III)>

¹³C-NMR Measurement Conditions

NMR apparatus: ECA500 manufactured by JEOL Resonance Co., Ltd.Probe: C5HPD/FG probeObserved range: −25 ppm to 225 ppmObservation center: 100 ppmPulse repetition time: 4 secPulse width: 45°NMR sample tube: 10 φSample amount: 250 mg to 300 mgSolvent: deuterochloroformMeasurement temperature: room temperatureNumber of scans: 10,000 times

The amount of a block represented by the formula (III) is calculatedfrom the area A of the signal peak of a carbonate bond of the blockrepresented by the formula (III), the peak being detected at 150.9 ppmwith respect to tetramethylsilane (TMS) in a ¹³C-NMR chart measuredunder the above-mentioned conditions, and the area B of a signal peak at152.1 ppm detected in the chart as a result of the overlapping of thesignals of a carbonate bond of a block represented by the formula (I-a)and a block represented by the formula (III-a) by using the calculationexpression “A/(A+B)” (unit: mol %).

The quantification lower limit of the quantification method wascalculated to be less than 0.1 mol % by the baseline SN ratio of the¹³C-NMR chart:

wherein R¹, R², R³¹ to R³⁵, X, “a”, “b”, and “t” are as described above.

(2) Viscosity-Average Molecular Weight

A viscosity-average molecular weight (Mv) was calculated from thefollowing equation (Schnell's equation) by using a limiting viscosity[η] determined through the measurement of the viscosity of a methylenechloride solution at 20° C. with an Ubbelohde-type viscometer.

[η]=1.23×10⁻⁵ ×Mv ^(0.83)

(3) Weight-Average Molecular Weight and Molecular Weight Distribution

The weight-average molecular weight (Mw) and molecular weightdistribution (Mw/Mn) of a PC-POS copolymer were measured with ahigh-performance GPC apparatus HLC-8220 GPC (manufactured by TosohCorporation) under the following conditions, and were calculated on thebasis of a general-purpose calibration curve produced by using amolecular weight standard sample.

Column temperature: 40° C.

Column: TSK-GEL GHXL-L, TSK-GEL G4000HXL, and TSK-GEL G2000HXL(manufactured by Tosoh Corporation)

Mobile phase solvent: tetrahydrofuran

Flow rate: 1.0 ml/min

Detector: RI

Injection concentration: 10 mg/10 ml

Injection volume: 0.1 ml

Molecular weight standard sample: Polycarbonate 18,050 (manufactured byIdemitsu Kosan Co., Ltd., molecular weight error: ±5%/17,148 to 18,953)and Polycarbonate 18,100 (manufactured by Idemitsu Kosan Co., Ltd.,molecular weight error: ±5%/17,200 to 19,100)

(4) Durometer Hardness

The type A durometer hardness of a molded body was measured with arubber hardness meter ESA type (manufactured by Elastron, Inc.) and aconstant loader EDL-1 (manufactured by Elastron, Inc.) in conformitywith JIS K 6253-3:2012 Type A and ISO 7619 Type A under a load of 1 kg.

The type D durometer hardness of a molded body was measured with arubber hardness meter ESD type (manufactured by Elastron, Inc.) and aconstant loader EDL-1 special type (with an oil damper, manufactured byElastron, Inc.) in conformity with JIS K 6253-3:2012 Type D and ISO 7619Type D under a load of 5 kg.

(5) Total Light Transmittance

The total light transmittance of a molded body when molded into athickness of 2 mm was measured with a haze meter NDH 5000 (manufacturedby Nippon Denshoku Industries Co., Ltd.) in conformity with JIS K7361-1:1997.

<Production of Polycarbonate Oligomer>

Sodium dithionite was added in an amount of 2,000 ppm with respect tobisphenol A (BPA) (to be dissolved later) to 5.6 mass % aqueous sodiumhydroxide, and then BPA was dissolved in the mixture so that theconcentration of BPA was 13.5 mass %. Thus, a solution of BPA in aqueoussodium hydroxide was prepared. The solution of BPA in aqueous sodiumhydroxide, methylene chloride, and phosgene were continuously passedthrough a tubular reactor having an inner diameter of 6 mm and a tubelength of 30 m at flow rates of 40 L/hr, 15 L/hr, and 4.0 kg/hr,respectively. The tubular reactor had a jacket portion and thetemperature of the reaction liquid was kept at 40° C. or less by passingcooling water through the jacket. The reaction liquid that had exitedthe tubular reactor was continuously introduced into a baffled vesseltype reactor provided with a sweptback blade and having an internalvolume of 40 L. The solution of BPA in aqueous sodium hydroxide, 25 mass% aqueous sodium hydroxide, water, and a 1 mass % aqueous solution oftriethylamine were further added to the reactor at flow rates of 2.8L/hr, 0.07 L/hr, 17 L/hr, and 0.64 L/hr, respectively, to perform areaction. An aqueous phase was separated and removed by continuouslytaking out the reaction liquid overflowing the vessel type reactor andleaving the reaction liquid at rest. Then, a methylene chloride phasewas collected.

The polycarbonate oligomer thus obtained had a concentration of 341 g/Land a chloroformate group concentration of 0.71 mol/L.

Production Example 1

185 mL of the polycarbonate oligomer solution (PCO) produced asdescribed above, 445 mL of methylene chloride, 30.3 g of an allylphenolterminal-modified polydimethylsiloxane having an average chain length“n” of 37, and 0.104 mL (0.75 mmol) of triethylamine (TEA) were loadedinto a 1-liter separable flask including a baffle board and a mechanicalstirrer with a stirring blade. Aqueous sodium hydroxide A (NaOHaq)(sodium hydroxide: 1.9 g (47 mmol), ion-exchanged water: 22 mL) preparedin advance was added to the mixture under stirring to perform a reactionbetween the polycarbonate oligomer and the allylphenol terminal-modifiedPDMS for 20 minutes. Next, aqueous sodium hydroxide B [BisP-AP(manufactured by Honshu Chemical Industry Co., Ltd.): 4.8 g (16 mmol),sodium hydroxide: 2.9 g (73 mmol), ion-exchanged water: 42 mL, sodiumhyposulfite (Na₂S₂O₄): 0.006 g (0.038 mmol)] prepared in advance wasfurther added to the resultant to advance polymerization for 20 minutes.

A solution of p-tert-butylphenol (PTBP: manufactured by DIC Corporation)in methylene chloride [obtained by dissolving 1.5 g (10.0 mmol) of PTBPin 10 mL of methylene chloride] and a solution C of BPA in aqueoussodium hydroxide [obtained by dissolving 7.4 g (26 mmol) of bisphenol A,5.2 g (131 mmol) of NaOH, and 0.006 g (0.038 mmol) of Na₂S₂O₄ in 77 mLof ion-exchanged water] were added to the resultant polymerizationliquid to perform a polymerization reaction for 20 minutes.

After the completion of the polymerization, the reaction liquid wastransferred to a separating funnel, and was left at rest to be separatedinto an organic phase and an aqueous phase. After that, the organiclayer was transferred to another separating funnel. The organic layerwas sequentially washed with 100 mL of 0.03 mol/L aqueous NaOH and 100mL of 0.2 mol/L hydrochloric acid, and was then repeatedly washed withion-exchanged water until an electric conductivity in an aqueous phaseafter the washing became 10 μS/m or less.

The organic layer obtained after the washing was transferred to a vat,and was dried in an explosion-proof dryer (under a nitrogen atmosphere)at 48° C. overnight. Thus, a sheet-shaped PC-POS copolymer was obtained.The sheet-shaped PC-POS copolymer was cut to provide a flaky PC-POScopolymer (a1). Details about the PC-POS copolymer are shown in Table1-1.

Production Example 2

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 40.4 g; a solution obtained bydissolving 1.9 g (47 mmol) of NaOH in 22 mL of ion-exchanged water wasused as the aqueous sodium hydroxide A; a solution obtained bydissolving 4.8 g (20 mmol) of BisP-B, 2.9 g (73 mmol) of NaOH, and 0.031g (0.20 mmol) of Na₂S₂O₄ in 42 mL of ion-exchanged water was used as theaqueous sodium hydroxide B; and a solution obtained by dissolving 3 g(10 mmol) of BPA, 5.2 g (131 mmol) of NaOH, and 0.031 g (0.20 mmol) ofNa₂S₂O₄ in 77 mL of ion-exchanged water was used as the solution C ofBPA in aqueous sodium hydroxide. Thus, a PC-POS copolymer (a6) wasobtained. Details about the PC-POS copolymer are shown in Table 1-1.

Production Example 3

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 40.4 g; and a solution obtained bydissolving 3.0 g (10 mmol) of bisphenol A, 5.2 g (131 mmol) of NaOH, and0.006 g (0.038 mmol) of Na₂S₂O₄ in 77 mL of ion-exchanged water was usedas the solution C of BPA in aqueous sodium hydroxide. Thus, a PC-POScopolymer (a2) was obtained. Details about the PC-POS copolymer areshown in Table 1-1.

Production Example 4

Production was performed in the same manner as in Production Example 1except that: 43.0 g of an allylphenol terminal-modifiedpolydimethylsiloxane having an average chain length “n” of 23 was usedas an allylphenol terminal-modified polydimethylsiloxane; a solutionobtained by dissolving 3.7 g (94 mmol) of NaOH in 43 mL of ion-exchangedwater was used as the aqueous sodium hydroxide A; a mixture of 5.5 g (19mmol) of BisP-AP (manufactured by Honshu Chemical Industry Co., Ltd.),2.3 g (57 mmol) of NaOH, 33 mL of ion-exchanged water, and 0.031 g(0.196 mmol) of Na₂S₂O₄ was used as the aqueous sodium hydroxide B; anda solution obtained by dissolving 2.5 g (8.7 mmol) of bisphenol A, 1.9 g(46.3 mmol) of NaOH, and 0.031 g (0.196 mmol) of Na₂S₂O₄ in 27 mL ofion-exchanged water was used as the solution C of BPA in aqueous sodiumhydroxide. Thus, a PC-POS copolymer (a10) was obtained. Details aboutthe PC-POS copolymer are shown in Table 1-1.

Production Example 5

Production was performed in the same manner as in Production Example 1except that: 46.0 g of an allylphenol terminal-modifiedpolydimethylsiloxane having an average chain length “n” of 63 was usedas an allylphenol terminal-modified polydimethylsiloxane; a solutionobtained by dissolving 2.2 g (55.9 mmol) of NaOH in 26 mL ofion-exchanged water was used as the aqueous sodium hydroxide A; amixture of 5.8 g (20 mmol) of BisP-AP (manufactured by Honshu ChemicalIndustry Co., Ltd.), 2.4 g (60 mmol) of NaOH, 35 mL of ion-exchangedwater, and 0.031 g (0.196 mmol) of Na₂S₂O₄ was used as the aqueoussodium hydroxide B; and a solution obtained by dissolving 6.6 g (22.6mmol) of bisphenol A, 3.2 g (80.9 mmol) of NaOH, and 0.031 g (0.196mmol) of Na₂S₂O₄ in 47 mL of ion-exchanged water was used as thesolution C of BPA in aqueous sodium hydroxide. Thus, a PC-POS copolymer(a14) was obtained. Details about the PC-POS copolymer are shown inTable 1-1.

Production Example 6

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 62.0 g; a solution obtained bydissolving 3.1 g (77 mmol) of NaOH in 35 mL of ion-exchanged water wasused as the aqueous sodium hydroxide A; a solution obtained bydissolving 6.0 g (21 mmol) of BisP-AP, 2.5 g (62 mmol) of NaOH, and0.031 g (0.20 mmol) of Na₂S₂O₄ in 36 mL of ion-exchanged water was usedas the aqueous sodium hydroxide B; and a solution obtained by dissolving4.0 g (14 mmol) of bisphenol A, 2.3 g (58 mmol) of NaOH, and 0.031 g(0.20 mmol) of Na₂S₂O₄ in 34 mL of ion-exchanged water was used as thesolution C of BPA in aqueous sodium hydroxide. Thus, a PC-POS copolymer(a3) was obtained. Details about the PC-POS copolymer are shown in Table1-1.

Production Example 7

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 77.0 g; a solution obtained bydissolving 3.5 g (87 mmol) of NaOH in 40 mL of ion-exchanged water wasused as the aqueous sodium hydroxide A; a solution obtained bydissolving 6.0 g (21 mmol) of BisP-AP, 2.5 g (62 mmol) of NaOH, and0.031 g (0.20 mmol) of Na₂S₂O₄ in 36 mL of ion-exchanged water was usedas the aqueous sodium hydroxide B; and a solution obtained by dissolving2.9 g (10 mmol) of bisphenol A, 1.9 g (48 mmol) of NaOH, and 0.031 g(0.20 mmol) of Na₂S₂O₄ in 28 mL of ion-exchanged water was used as thesolution C of BPA in aqueous sodium hydroxide. Thus, a PC-POS copolymer(a4) was obtained. Details about the PC-POS copolymer are shown in Table1-1.

Production Example 8

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 96.0 g; a solution obtained bydissolving 4.0 g (100 mmol) of NaOH in 46 mL of ion-exchanged water wasused as the aqueous sodium hydroxide A; a solution obtained bydissolving 7.7 g (27 mmol) of BisP-AP, 4.7 g (118 mmol) of NaOH, and0.031 g (0.20 mmol) of Na₂S₂O₄ in 69 mL of ion-exchanged water was usedas the aqueous sodium hydroxide B; and the solution C of BPA in aqueoussodium hydroxide was not added. Thus, a PC-POS copolymer (a5) wasobtained. Details about the PC-POS copolymer are shown in Table 1-1.

Production Example 9

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 4.0 g; a solution obtained bydissolving 1.5 g (38 mmol) of NaOH in 18 mL of ion-exchanged water wasused as the aqueous sodium hydroxide A; 1.8 g (12.0 mmol) of PTBP wasused; a solution obtained by dissolving 13.2 g (45 mmol) of bisphenol A,6.3 g (159 mmol) of NaOH, and 0.031 g (0.20 mmol) of Na₂S₂O₄ in 93 mL ofion-exchanged water was used as the solution C of BPA in aqueous sodiumhydroxide; and the aqueous sodium hydroxide B was not loaded. Thus, aPC-POS copolymer (a9) was obtained. Details about the PC-POS copolymerare shown in Table 1-2.

Production Example 10

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 23.0 g; a solution obtained bydissolving 2.0 g (50.8 mmol) of NaOH in 23 mL of ion-exchanged water wasused as the aqueous sodium hydroxide A; 1.8 g (12.0 mmol) of PTBP wasused; a solution obtained by dissolving 11.7 g (40.4 mmol) of bisphenolA, 5.8 g (146.0 mmol) of NaOH, and 0.031 g (0.20 mmol) of Na₂S₂O₄ in 85mL of ion-exchanged water was used as the solution C of BPA in aqueoussodium hydroxide; and the aqueous sodium hydroxide B was not loaded.Thus, a PC-POS copolymer (a12) was obtained. Details about the PC-POScopolymer are shown in Table 1-2.

Production Example 11

Production was performed in the same manner as in Production Example 1except that: 30.0 g of an allylphenol terminal-modifiedpolydimethylsiloxane having an average chain length “n” of 63 was usedas an allylphenol terminal-modified polydimethylsiloxane; a solutionobtained by dissolving 1.8 g (45 mmol) of NaOH in 21 mL of ion-exchangedwater was used as the aqueous sodium hydroxide A; 1.8 g (12.0 mmol) ofPTBP was used; a solution obtained by dissolving 12.3 g (43 mmol) ofbisphenol A, 6.1 g (151 mmol) of NaOH, and 0.031 g (0.20 mmol) ofNa₂S₂O₄ in 89 mL of ion-exchanged water was used as the solution C ofBPA in aqueous sodium hydroxide; and the aqueous sodium hydroxide B wasnot loaded. Thus, a PC-POS copolymer (a8) was obtained. Details aboutthe PC-POS copolymer are shown in Table 1-2.

Production Example 12

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 55 g; a solution obtained bydissolving 2.9 g (72.1 mmol) of NaOH in 33 mL of ion-exchanged water wasused as the aqueous sodium hydroxide A; 1.8 g (12.0 mmol) of PTBP wasused; a solution obtained by dissolving 9.3 g (32.0 mmol) of bisphenolA, 5.0 g (124.7 mmol) of NaOH, and 0.031 g (0.20 mmol) of Na₂S₂O₄ in 73mL of ion-exchanged water was used as the solution C of BPA in aqueoussodium hydroxide; and the aqueous sodium hydroxide B was not loaded.Thus, a PC-POS copolymer (a13) was obtained. Details about the PC-POScopolymer are shown in Table 1-2.

Production Example 13

Production was performed in the same manner as in Production Example 1except that: the amount of the allylphenol terminal-modifiedpolydimethylsiloxane was changed to 78.0 g; a solution obtained bydissolving 3.5 g (87 mmol) of NaOH in 40 mL of ion-exchanged water wasused as the aqueous sodium hydroxide A; 1.8 g (12.0 mmol) of PTBP wasused; a solution obtained by dissolving 7.5 g (26 mmol) of bisphenol A,4.4 g (109 mmol) of NaOH, and 0.031 g (0.20 mmol) of Na₂S₂O₄ in 70 mL ofion-exchanged water was used as the solution C of BPA in aqueous sodiumhydroxide; and the aqueous sodium hydroxide B was not loaded. Thus, aPC-POS copolymer (a7) was obtained. Details about the PC-POS copolymerare shown in Table 1-2.

TABLE 1-1 Production Example 1 2 3 4 5 6 7 8 Amount of PDMS in PC-POSmass % 32 39 40 41 42 50 56 62 copolymer (A) Amount of BPA block in PCmass % 92.4 92.3 92.2 92.8 90.0 90.9 93.3 95.0 block (A-1)*¹ PC block(A-1) except BPA*² BisP-AP BisP-B BisP-AP BisP-AP BisP-AP BisP-APBisP-AP BisP-AP Amount of PC block except mass % 5 5 5 4 5 5 3 2 BPA inPC-POS copolymer (A)*2 Amount of block represented mol % <0.1 <0.1 <0.1<0.1 <0.1 <0.1 <0.1 <0.1 by formula (III) in PC-POS copolymer (A) PDMSchain length 37 37 37 23 63 37 37 37 Mv 22,500 20,200 20,000 17,90020,500 19,200 18,300 19,400 Mw — — 28,000 — — — — 34,400 Molecularweight distribution — — 2.5 — — — — 2.8 (Mw/Mn) PC-POS copolymer a1 a6a2 a10 a14 a3 a4 a5 *¹BPA block: the term represents a PC block derivedfrom BPA. *²PC block except BPA: the term represents a PC block derivedfrom a dihydric phenol except BPA.

TABLE 1-2 Production Example 9 10 11 12 13 Amount of PDMS in PC-POScopolymer (A) mass % 6 25 30 45 55 Amount of BPA block in PC block(A-1)*¹ mass % 100 100 100 100 100 PC block (A-1) except BPA*2 — — — — —Amount of PC block except BPA in PC-POS copolymer (A)*² mass % — — — — —Amount of block represented by formula (III) in PC-POS mol % <0.1 <0.1<0.1 <0.1 <0.1 copolymer (A) PDMS chain length 37 37 63 37 37 Mv 17,70017,600 17,600 17,500 16,500 Mw — 20,700 21,000 24,700 36,700 Molecularweight distribution (Mw/Mn) — 2.3 2.4 2.6 2.9 PC-POS copolymer a9 a12 a8a13 a7 *¹BPA block: the term represents a PC block derived from BPA.*²PC block except BPA: the term represents a PC block derived from adihydric phenol except BPA.

Examples 1 to 12 and Comparative Example 1

Each of the PC-POS copolymers obtained in the respective productionexamples was molded with a vacuum press machine (manufactured by ImotoMachinery Co., Ltd., manual hydraulic vacuum heat press machine). 7.0 gof the resin was loaded into a mold measuring 5 cm long by 5 cm wide by2 mm thick, and a mirror-finished aluminum plate was brought intocontact with the surface of the resin to sandwich the resin between theplate and the mold. The resultant was loaded into the vacuum pressmachine, and a pressure in the tank of the vacuum press machine wasreduced to −0.1 MPa or less with respect to atmospheric pressure. Afterthat, the resin was heated to a molding temperature shown in each ofTable 2-1 and Table 2-2. After the temperature of the resin had reachedthe molding temperature, a press pressure was set to 2 MPa, and then theresin was heated for 2 minutes. Subsequently, the press pressure wasincreased over 3 minutes, and the molding was performed for 5 minuteswhile the pressure was maintained at 15 MPa. After the molding, thepressure in the tank was returned to atmospheric pressure, and then themolded body was removed and cooled to room temperature. After that, themolded body was peeled from the mirror-finished aluminum plate toprovide a sample for measurement measuring 5 cm long by 5 cm wide by 2mm thick. The evaluation results of the PC-POS copolymers are shown inTable 2-1 and Table 2-2.

TABLE 2-1 Example 1 2 3 4 5 6 7 8 PC-POS copolymer a1 a6 a2 a10 a14 a3a4 a5 Molding temperature of 280 280 280 280 280 280 280 280 sample fordurometer hardness measurement (° C.) Durometer hardness  67  62  63  60 51  47 33 29 Type D Durometer hardness    95<    95<    95<    95<   95<    95< 85 78 Type A Molding temperature of 180 180 180 230 230180 180 180 sample for total light transmittance measurement (° C.)Total light transmittance   90.0   90.1   90.8   91.2   81.2   91.4 91.291.7 (%)

TABLE 2-2 Comparative Example Example 9 10 11 12 1 PC-POS copolymer a12a8 a13 a7 a9 Molding temperature 280 280 280 280 280 of sample fordurometer hardness measurement (° C.) Durometer hardness  71  63  57 28 74 Type D Durometer hardness  95<  95<  95< 74  95< Type A Moldingtemperature 280 320 280 280 180 of sample for total light transmittancemeasurement (° C.) Total light   90.3   78.3   90.9 92.3   88.9transmittance (%)

INDUSTRIAL APPLICABILITY

According to the present invention, the molded body having both ofexcellent flexibility and transparency can be obtained. The molded bodyof the present invention may be used as an optical transparent member.Specifically, the molded body may be suitably used in at least oneselected from, for example, a flexible display, a light guide plate, ahousing, a water- or oil-repellent film, an optical adhesive, a switchcover, a heat sealing agent, a water stop material, a sealing agent, aconnector, an adapter, a smartphone cover, a lens, a part for a pair ofglasses or sunglasses, an optical fiber part, a cushion material for anon-vehicle battery, a wiper blade, a traffic mirror, a side mirror, arearview mirror, a lamp cover, a bumper, a window, an exterior material,an interior material, an acoustic material, a steering wheel cover, asensor cover, a watch part, stationery, a cosmetic container, anaquarium for rearing an aquatic organism, a sole, a cup, a nail artmaterial, a toy, a lure, a suction cup, cooking tools including asteamer, clothes, a silicone wiping sheet, a remote controller cover, anumbrella, a metal container lining, a building material cover, a door, awindow, a glass interlayer, a tent, a mirror, a shop window case, aplastic greenhouse, a medical equipment housing, a transfusion bag, atransfusion tube, an injection syringe, a feeding bottle, a mask, a facebelt, a filter part, a damping part, a robot housing, a drone housing, ashield, a bulletproof shield, a sport cushion, a window for an aircraft,a resin compatibilizer, a lighting cover, a light guide, a light guidepanel, a lighting unit, a prism panel, a flat lens, a Fresnel lens, amicrolens array, and a collimator lens.

1. A molded body, comprising a polycarbonate-polyorganosiloxanecopolymer (A) which contains a polycarbonate block (A-1) formed of arepeating unit represented by the following general formula (I) and apolyorganosiloxane block (A-2) containing a repeating unit representedby the following general formula (II), and in which a content of thepolyorganosiloxane block (A-2) is from 20 mass % or more to 70 mass % orless, wherein the molded body has a durometer hardness of from 25 ormore to 72 or less measured with a type D durometer in conformity withJIS K 6253-3:2012:

wherein R¹ and R² each independently represent a halogen atom, an alkylgroup having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6carbon atoms, X represents a single bond, an alkylene group having 1 to8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, acycloalkylene group having 5 to 15 carbon atoms, an arylene group having6 to 12 carbon atoms, a cycloalkylidene group having 5 to 15 carbonatoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbonatoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—,—SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogenatom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, analkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12carbon atoms, and “a” and “b” each independently represent an integer offrom 0 to
 4. 2. The molded body according to claim 1, wherein a contentof a unit represented by the following general formula (III) in thepolyorganosiloxane block (A-2) is 0.1 mol % or less:

wherein R³³ and R³⁴ each independently represent a hydrogen atom, ahalogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy grouphaving 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbonatoms, R³¹ represents an alkylene group having 1 to 8 carbon atoms, analkylidene group having 2 to 8 carbon atoms, a cycloalkylene grouphaving 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15carbon atoms, an arylene group having 6 to 12 carbon atoms, afluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms,or an arylalkylidene group having 7 to 15 carbon atoms, R³⁵ represents ahydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbonatoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl grouphaving 6 to 12 carbon atoms, and “t” represents an average chain lengthof a polyorganosiloxane.
 3. The molded body according to claim 1,wherein the polyorganosiloxane block (A-2) has a number of repetitionsof from 10 or more to less than
 90. 4. The molded body according toclaim 1, wherein the polyorganosiloxane block (A-2) contains a unitrepresented by at least one of the following general formula (II-I),(II-II), or (II-III):

wherein R³ to R⁶ each independently represent a hydrogen atom, a halogenatom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and aplurality of R³s, R⁴s, R⁵s, or R⁶s may be identical to or different fromeach other, Y represents —R⁷O—, —R⁷COO—, —R⁷NH—, —R⁷NR⁸—, —COO—, —S—,—R⁷COO—R⁹—O—, or —R⁷O—R¹⁰-O—, and a plurality of Ys may be identical toor different from each other, the R⁷ represents a single bond, a linear,branched, or cyclic alkylene group, an aryl-substituted alkylene group,a substituted or unsubstituted arylene group, or a diarylene group, R⁸represents an alkyl group, an alkenyl group, an aryl group, or anaralkyl group, R⁹ represents a diarylene group, R¹⁰ represents a linear,branched, or cyclic alkylene group, or a diarylene group, β represents adivalent group derived from a diisocyanate compound, or a divalent groupderived from a dicarboxylic acid or a halide of a dicarboxylic acid, “n”represents a chain length of a polyorganosiloxane, and n−1, and “p” and“q” each represent a number of repetitions of a polyorganosiloxane unitand each represent an integer of 1 or more, and a sum of “p” and “q” isn−2.
 5. The molded body according to claim 1, wherein thepolyorganosiloxane block (A-2) is represented by the following generalformula (V):

wherein R³ to R⁶ and n−1 are the same as those described in the generalformulae (II-I) to (II-III), and R¹⁵ represents a hydrogen atom, ahalogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy grouphaving 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbonatoms.
 6. The molded body according to claim 1, wherein thepolycarbonate-polyorganosiloxane copolymer (A) has a viscosity-averagemolecular weight of from 10,000 or more to 23,000 or less.
 7. The moldedbody according to claim 1, wherein the polycarbonate-polyorganosiloxanecopolymer (A) has a molecular weight distribution of from 2.1 or more to3.9 or less.
 8. The molded body according to claim 1, wherein the moldedbody has a total light transmittance of 75% or more measured inconformity with JIS K 7361-1:1997 when molded into a thickness of 2 mm.9. The molded body according to claim 1, wherein the molded body is anoptical member.
 10. The molded body according to claim 1, wherein themolded body is at least one selected from a flexible display, a lightguide plate, a housing, a water- or oil-repellent film, an opticaladhesive, a switch cover, a heat sealing agent, a water stop material, asealing agent, a connector, an adapter, a smartphone cover, a lens, apart for a pair of glasses or sunglasses, an optical fiber part, acushion material for an on-vehicle battery, a wiper blade, a trafficmirror, a side mirror, a rearview mirror, a lamp cover, a bumper, awindow, an exterior material, an interior material, an acousticmaterial, a steering wheel cover, a sensor cover, a watch part,stationery, a cosmetic container, an aquarium for rearing an aquaticorganism, a sole, a cup, a nail art material, a toy, a lure, a suctioncup, cooking tools including a steamer, clothes, a silicone wipingsheet, a remote controller cover, an umbrella, a metal container lining,a building material cover, a door, a window, a glass interlayer, a tent,a mirror, a shop window case, a plastic greenhouse, a medical equipmenthousing, a transfusion bag, a transfusion tube, an injection syringe, afeeding bottle, a mask, a face belt, a filter part, a damping part, arobot housing, a drone housing, a shield, a bulletproof shield, a sportcushion, a window for an aircraft, a resin compatibilizer, a lightingcover, a light guide, a light guide panel, a lighting unit, a prismpanel, a flat lens, a Fresnel lens, a microlens array, and a collimatorlens.